Diameter: 0.8m-2.0m
Length: 5.0m-18m
Layers: 4-10
Characteristic: Anti-Explosion, Flexible, High Bearing Capacity,
Warranty: 24 Months
Working Age: More Than 10 Years
Trademark: DACHENG
Transport Package: Natural Rubber & Synthetic Cord Layer
Specification: as drawings
Origin: China
HS Code: 4016950090
Introduction
Ship launching airbags are to be constructed of a cylindrical body and two conical heads (one at each end). Ship launching airbags with lots of advantages, such as easy to operate, time saving, saving investment safety, etc.
Major Strengths of Ship Launching Airbags:
High level of safety: Equipped with a reliable safety valve, our airbags can stand the maximum pressure up to 4 times that of the operating pressure.
Good air tightness: Pressure decreases less than 10% for a period of 24 hours.
Long lifespan: It is guaranteed that our airbags can sustain their designed operating pressure for 3 years.
Specification
1. Structure
2. Diameters: 0.8 m - 2.0 m or customized.3. Length: 6 m - 20 m or customized.
4. Loading Capacity: about 10 T/M to 40 T/M.
5. Grades:
Ordinary airbags - 3, 4 or 5 layers of synthetic-tire-cord.
High bearing capacity airbags - 6, 7 or 8 synthetic-tire-cord.
Super high bearing capacity airbags - 9, 10 or more layers of synthetic-tire-cord.
6. Accessories: Pull ring, iron airlock, tee joint, pressure gauge, ball valve, hose joint etc.
7. Technical Data of Ship Launching Airbags
Model |
Diameter (m) |
Initial pressure (KPa) |
Rated working pressure, Pe (KPa) |
Bearing capacity (kN/m) |
Minimum burst pressure (KPa) |
QP3 |
0.8 |
25 |
130 |
114 |
390 |
1.0 |
18 |
100 |
110 |
300 |
1.2 |
15 |
85 |
112 |
260 |
1.5 |
13 |
70 |
115 |
210 |
QP4 |
0.8 |
35 |
170 |
149 |
510 |
1.0 |
25 |
130 |
143 |
390 |
1.2 |
20 |
110 |
145 |
330 |
1.5 |
16 |
90 |
148 |
270 |
1.8 |
14 |
80 |
158 |
240 |
QP5 |
0.8 |
48 |
210 |
184 |
630 |
1.0 |
35 |
170 |
186 |
510 |
1.2 |
28 |
140 |
185 |
420 |
1.5 |
20 |
110 |
181 |
330 |
1.8 |
16 |
90 |
178 |
270 |
QP6 |
1.0 |
45 |
200 |
219 |
600 |
1.2 |
32 |
165 |
217 |
490 |
1.5 |
25 |
130 |
215 |
390 |
1.8 |
20 |
110 |
218 |
330 |
Note: 1. Rated working pressure:±5%. 2. Compress deformation: ±2%. 3. Bearing capacity: one meter airbag at a deformation rate of 70%, internal pressure equivalent to the rated pressure value of Pe. |
8. Material: A ship lunching airbag is to be constructed of an outer rubber layer, one or more synthetic-tyre-cord layers, and an inner rubber layer. All material layers should be vulcanized firmly.
9. Rubber Material Test:
No. |
Test item |
Required value |
Test method |
1 |
Tensile Strength, MPa |
≥ 18 |
ISO37 |
2 |
Elongation at break, % |
≥ 400 |
ISO37 |
3 |
Hardness, shore A |
60±10 |
ISO7619-1 |
4 |
Tear Strength N/cm |
≥ 400 |
ISO34-1 |
5 |
Compression set, % (70 ºC ± 1 ºC, 22 h) |
≤ 30 |
ISO815-1 |
6 |
After thermal aging at (70 ºC, ±1 ºC, 96 h) |
Holding of pull lengthening,% |
≥ 80 |
ISO188 |
7 |
Holding of elongation at break,% |
≥ 80 |
ISO188 |
8 |
Change of hardness, hardness |
≤ 8 |
ISO7619-1 |
9 |
Static ozone aging at 40 ºC*96 h, {ozone concentration( 50±5)*10} |
No crack |
ISO1431-1 |
Â
10. Reinforcing Material: the warp should be (90±5) cord per 100 mm in width, and the breaking strength shall be more than 205 N per cord.
Â
11. Appearance: The appearance of an air bag shall be smooth, glossy and without blemish such as crack, blister, delamination pits or impurities.
Â
12. Dimensional Tolerances:
The length and diameter of an airbag shall be measured with the rated working pressure and be within ±3%.
Â
13. Ship Launching Airbags Performance:
D (M) |
(4-5 layers) |
(6-8 layers) |
 |
Initial pressure (MPa) |
Working pressure (MPa) |
Initial pressure (MPa) |
Working pressure (MPa) |
 |
 |
1.0 |
0.14 - 0.16 |
0.12 - 0.14 |
0.22 - 0.26 |
0.20 - 0.24 |
 |
1.2 |
0.12 - 0.14 |
0.10 - 0.12 |
0.20 - 0.24 |
0.17 - 0.22 |
 |
1.5 |
0.10 - 0.12 |
0.08 - 0.10 |
0.15 - 0.20 |
0.13 - 0.18 |
 |
1.8 |
0.08 - 0.10 |
0.07 - 0.09 |
0.13 - 0.16 |
0.11 - 0.14 |
 |
2.0 |
0.07 - 0.09 |
0.06 - 0.08 |
0.12 - 0.15 |
0.10 - 0.13 |
 |
Â
Â
The design of middle through hole is easy to install, Barrel Damper is usually used in small spaces. ABD barrel dampers are the perfect solution for a wide range of applications. Barrel dampers are widely used in automobile interior decoration, household electric appliances, furniture, hidden socket, etc. Our dampers can make the movement of structures soft, quiet and safe to mitigate the impact, avoid the damage, increase the mechanical life, reduce noise, and improve product quality.
NOTE:
1. Please contact the corresponding product
engineer for specific torque products.
2. Max. rotation speed: 50r/min
3. Max. circle rate: Clockwise180 °, 180 ° anti-clockwise for 1
cycle
4. Operating temperature: -10~50℃
5. Storage temperature:-30~60℃
Applied torque:(T)
Test Temperature:23+/-5℃
Rotating speed:20r/min
Durability test Method:Clockwise 180 °, 180 ° anti-clockwise
Rotating speed:20r/min
Test Frequency:1cycle/min
Test Temperature:23±5℃
Durability test cycle:10000 cycle
Test result criteria: Store in the room temperature for 24 hours or more after the test, recording to the torque T=T±30%T.